CuAl10Fe3Mn2 Aluminium Bronze
CuAl10Fe3Mn2 aluminium bronze, supplied as solid bar, hollow bar (bushes), flat bar and plate, and as castings made to pattern. Manganese- and iron-bearing aluminium bronze (EN 12163: 9–11% Al, 2–4% Fe, 1.5–3.5% Mn).
Grade and sizes
CuAl10Fe3Mn2
Manganese- and iron-bearing aluminium bronze (EN 12163: 9–11% Al, 2–4% Fe, 1.5–3.5% Mn). It offers high corrosion resistance and good hot formability and is produced extruded or forged. It is used for bearings and bushes, gears, cams, guides and slides, valve seats and valve guides.
Rod standard: EN 12163 · forgings: EN 12420
- FORMS
- Solid bar, hollow bar (bushes), flat bar and plate; castings to pattern
- PRODUCTION
- Bar, bushes and flat bar are extruded or forged; parts to pattern are produced as castings
- SIZE
- To order
- ORDERING
- Cut to size, minimum 5 kg
For large-quantity orders, other cut sizes are possible.
Weight calculator
Calculate the weight from the size, or the length and number of pieces needed for a target weight. Your selections are added to the quote message automatically.
Size: Ø50 × 400 mm, quantity: 1 (theoretical ~5.97 kg)
Technical data
Chemical composition, mechanical properties and material certificates are available on request.
+90 530 671 13 78 · info@pointmetal.com.tr
Applications
- Bearings and bushes
- Gears and cams
- Guides and slides
- Valve seats and valve guides
- Hot-forged parts
Frequently asked questions
How is the right aluminium bronze grade chosen?
Where seawater, cavitation and high strength come together, the nickel grades (CuAl10Ni5Fe4, CuAl10Ni) are preferred. Where heavy load and wear dominate, the harder CuAl11Ni6Fe5 or CuAl11Ni is used, and CuAl14Fe4Mn2 for very high loads and tooling. For general wear applications that do not need nickel, CuAl10Fe and CuAl10Fe3Mn2 are economical choices. If you send us the part and its operating conditions, we will work out the right grade with you.
What is the difference between wrought (extruded) and cast aluminium bronze?
Grades produced by extrusion or forging (CW numbers) have a more uniform, porosity-free structure and are preferred for shafts and parts needing high strength. Cast grades (CC numbers or DIN 1714) are an economical choice for large-diameter bushes, rings and parts made to pattern.
Do you supply castings to pattern?
Yes. If you send a drawing or sample part together with the quantity and grade, we prepare a quotation for castings to pattern. For simple shapes such as bushes and rings, machining from hollow bar is often more economical.
What is the difference between aluminium bronze and tin bronze?
Aluminium bronzes offer higher strength, hardness and seawater resistance and suit parts working under heavy load, impact and wear. Tin bronzes stand out for lubricated bushes, bearings and gears thanks to their better sliding properties.
What are the designations for CuAl10Fe3Mn2?
CuAl10Fe3Mn2: EN CW306G, DIN 2.0936, close to UNS C62400. Any of these designations can be used in your enquiry; we will match the correct material.
Why can the invoiced weight differ from the calculated weight?
The calculator gives the theoretical weight. The actual weight varies with dimensional tolerances and cutting allowance; we invoice on the actual weight as weighed.
What information should I send for a quote?
We only need the size (diameter × length), quantity and delivery location. If you fill in the calculator above, these details are added to the WhatsApp message automatically.